Description
Inherently conductive polymer.
Stable at 100 °C and at 200 °C for short periods. Dispersed particles tend to reaggregrate in molded articles forming conductive pathways. Acidic salt of an organic acid, incompatible with most bases.
Form of polyaniline complexed (doped) with proprietary organic sulfonic acid
Form of polyaniline complexed (doped) with proprietary organic sulfonic acid. Polyaniline is environmentally stable and with tunable conductivity. Synthesis of polyaniline (PANI) emeraldine salt by chemical oxidation has been reported. It was observed that sulfonated dyes chemically interact with the charged backbone of PANI. PANI selectively adsorbs the sulfonated dye. Spectral, diffraction and conductivity measurements of the polymer has been reported in the same study.
Stable at 100 °C and at 200 °C for short periods. Dispersed particles tend to reaggregrate in molded articles forming conductive pathways. Acidic salt of an organic acid, incompatible with most bases.
Form of polyaniline complexed (doped) with proprietary organic sulfonic acid
Form of polyaniline complexed (doped) with proprietary organic sulfonic acid. Polyaniline is environmentally stable and with tunable conductivity. Synthesis of polyaniline (PANI) emeraldine salt by chemical oxidation has been reported. It was observed that sulfonated dyes chemically interact with the charged backbone of PANI. PANI selectively adsorbs the sulfonated dye. Spectral, diffraction and conductivity measurements of the polymer has been reported in the same study.
Synonyms
PANI
Molecular Weight
average Mw >15,000
Melting Point
>300 °C (lit.)
Density
1.36 g/mL at 25 °C
Appearance
powder (Infusible)
Storage
room temp
MDL Number
MFCD00284320
Specific Surface Area
5-20 m2/g
Unit Size
5g;25g